Extrudable thermoplastic elastomeric urea-extended polyurethane

ABSTRACT

An extrudable urea-extended thermoplastic polyurethane elastomer is formed from at least one aliphatic diisocyanate, at least one polyester glycol or polyether glycol, and at least one diamine curing agent. At least one second diamine curing agent and/or at least one extrusion processing aid may be included. The polyurethane has high-temperature-resistance and is thus extrudable at high temperatures. The polyurethane is also strong and durable. The polyurethane can be liquid-cast, injection-molded, transfer-molded, sprayed, and extruded without changing either the chemistry or stoichiometry of the polyurethane. The polyurethane may be used for making vehicle air bags or other any application for thermoplastic urethanes which requires increased thermal stability.

This application claims priority from U.S. Provisional patent application Ser. No. 60/018,042 filed May 21, 1996.

FIELD OF THE INVENTION

The present invention relates to an improved extrudable, thermoplastic, elastomeric polyurethane for use in efficiently manufacturing products such as air bags with excellent properties, and a process for making the same.

BACKGROUND OF THE INVENTION

New air bag technology demands a polyurethane elastomer which combines high-temperature resistance with excellent physical properties, processing parameters, and resistance to hydrolysis, oxygen, and ozone. In particular, for air bag use or any other related use, some of the most important properties are extrudability, high-temperature resistance, low temperature flex, high strength, elongation, low to moderate tensile modulus, good environmental resistance, excellent tear resistance, with an "A" durometer of about 80.

The extrudable urethane elastomers currently commercially available are typically hydroxyl-extended and do not have the thermal resistance necessary to resist the temperature of the gas generator during air bag deployment.

It is believed that there are currently no thermoplastic urethane elastomer compositions available that are urea-extended and that can be extruded with a combination of excellent temperature resistance, physical, and environmental properties. It has been believed in the art that a processable thermoplastic urethane could not be obtained using a diamine chain extender because the resulting urea segments gave the urethane a very high melting point. As such, the polyurethanes could not be processed by typical methods used in processing thermoplastic elastomeric materials, such as extrusion, without decomposition of the urethane.

Extrusion of thermoplastic polyurethane elastomers would be desirable to allow flexibility in the formation of various product shapes and sizes, including air bag bladders and the like. Extrusion also is a less expensive and faster processing method compared to other formation processes such as liquid casting.

Taub, U.S. Pat. No. 3,600,358, discloses a polyurethane elastomer prepared from a 4,4'-methylene bis(cyclohexylisocyanate), neopentyl adipate and aromatic diamine. Following addition of the aromatic diamine to the urethane prepolymer, the mixture is heated and poured into a mold for curing. Taub does not indicate that the urethane can be extruded. Taub also does not disclose or suggest the inclusion of a mixture of diamine materials to improve the extrudability of a urea-extended urethane.

Slagel, U.S. Pat. No. 3,866,242, discloses a protective shield comprising a polyurethane made from a polyester or polyether glycol, a diisocyanatodicyclohexylmethane isocyanate material, and a primary amine such as 4,4'-methylenebis(2-chloroaniline). The polyurethanes are cast between glass plates and cured to form the protective shield. The polyurethane disclosed by Slagel is not elastomeric, as evidenced by the disclosure that the material has a hardness on the "D" scale of 77-80 (col. 3, line 30). Slagel does not indicate that the polyurethane can be extruded. Slagel also does not disclose or suggest the inclusion of a mixture of diamine materials to improve the extrudability of a urea-extended urethane.

Accordingly, it is an object of the present invention to provide a thermoplastic polyurethane elastomer that is extrudable, that has high temperature resistance, and that is strong and durable for use in manufacturing urethane products such as air bags and the like. It is a further object of the present invention to provide a process for making such polyurethanes, as well as a process for extruding such polyurethanes.

Novel features of the invention, together with advantages thereof, will be better understood from the following descriptions in which embodiments of the invention are illustrated by way of examples.

SUMMARY OF THE INVENTION

Polyurethanes of the present invention comprise an extrudable reaction product of at least one aliphatic diisocyanate with at least one hydroxy-containing intermediate selected from polyester glycols, polyether glycols, and mixtures thereof, and at least one diamine curing agent. The polyurethanes may also include an extrusion processing aid. A process of the present invention comprises reacting at least one aliphatic diisocyanate with at least one hydroxy-containing intermediate to form a prepolymer, and then reacting the prepolymer with at least one diamine curing agent to form a thermoplastic polyurethane elastomer. Alternatively, at least one aliphatic diisocyanate may be reacted with less than one equivalent of the hydroxy-containing intermediate to form a prepolymer, and then the remaining equivalents of the hydroxy-containing intermediate may be added along with at least one diamine curing agent to form a cured elastomer. In addition, the present invention relates to a process of extruding polyurethanes of the invention, as well as extruded polyurethane products.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Polyurethanes of the present invention comprise a reaction product of at least one aliphatic diisocyanate with at least one hydroxy-containing intermediate selected from polyester glycols, polyether glycols, and mixtures thereof, and at least one diamine curing agent. Preferably, the diamine curing agent system is a mixture of at least one first diamine curing agent and at least one second diamine curing agent. However, the polyurethane may be cured with only the at least one first diamine curing agent. At least one extrusion processing aid may also be included in the polyurethane. The polyurethanes of the present invention are thermoplastic elastomers that can be readily extruded into various urethane products.

The present polyurethanes are extrudable due to possessing an excellent melt flow property while at the same time having high thermal stability. Compared to commercially available thermoplastic urethane elastomers having a Shore A hardness of about 80, polyurethanes according to the invention having a similar Shore A hardness have a lower melt flow temperature on the order of 10° to 70° C. lower, when measured according to the ASTM D-1238 method. The melt flow index of the polyurethanes of the present invention ranges from about 5 to 40 inches per minute, more preferably from about 8 to 25 inches per minute, when measured in accordance with the modified ASTM D-1238 method described in Example 9. Thus, embodiments of the inventive polyurethanes are extrudable within the range of about 215° C. to 310° C., preferably about 235° C. to 260° C. Commercially available polyurethanes, on the other hand, liquify at such processing temperatures. Typically, commercially available polyurethanes, such as Pellethane (a hydroxyl-extended extrudable grade polyurethane commercially available from Dow), are extruded through a melt flow indexer at temperatures of about 224° C., using a load of 2 to 6 kg. Higher extrusion temperatures cannot be used because these commercially available polyurethanes destabilize and liquify at higher temperatures. The polyurethanes of the present invention, however, can be extruded at very high temperatures without degradation.

Without wishing to be bound by theory, the inventor believes that the present urea extended polyurethanes possess such superior properties and are extrudable due to the polyurethane including an aliphatic diisocyanate, preferably a saturated aliphatic diisocyanate. As such, the polyurethane exhibits thermoplastic properties and does not form any side reactions, e.g. does not form biurets, upon curing, unlike polyurethanes formed with aromatic diisocyanates. The polyurethanes thus may be cured to a solid product with excellent properties, but also may be re-melted and re-extruded due to the absence and/or low level of biurets.

Water included in the process of making the polyurethane can cause side reactions, thereby degrading the extrudability of the polyurethane formed. It is thus preferred that the polyurethane starting materials contain a low amount of water, if any. For example, the polyurethane is preferably made in an environment containing water in an amount no more than 0.03 weight percent by weight of the polyurethane materials.

In addition to the aliphatic diisocyanate, the present properties and extrudability are also believed to be realized in part by the use of diamine chain extending agents. The urea extensions in the polyurethane chain provide the polyurethanes with superior thermal stability, as discussed above, permitting extrusion at high temperatures.

Diamine Curing Agents

The diamine curing agents, or chain extenders, are preferably primary amines. Preferably, the at least one diamine curing agent is a mixture of two or more diamine curing agents. Preferably, a first diamine curing agent is an amine having a high thermal stability and capable of providing excellent melt flow properties to the polyurethane. Examples of first diamine curing agents include 2,4-diamino-3,5-diethyl-toluene and 2,6-diamino-3,5-diethyl-toluene (collectively diethylene toluenediamine (DETDA)), methylene dianiline (MDA), and mixtures thereof. For example, a preferred first curing agent used in the process of the present invention is diethylene toluenediamine (DETDA), which is sold by the Albemarle Corporation under the trade name Ethacure 100. This diamine curing agent is a liquid at room temperature. It has the following formula: ##STR1##

Another preferred first diamine curing agent that may be used alone or in combination with other first diamine curing agents is methylene dianiline (MDA). MDA is available from Aldrich and has the following formula: ##STR2##

Although a good product is obtained using only the aforesaid first diamine curing agent(s), extrudability of the urethane polymer may be dramatically improved by adding a second diamine curing agent that acts as a reactive processing aid. For example, the second diamine curing agent may have the following formula: ##STR3## wherein R₁ and R₂ are each independently selected from methyl, ethyl, propyl, and isopropyl groups, and R₃ is selected from hydrogen and chlorine. Examples of these diamine curing agents include the following compounds manufactured by Lonza Ltd. (Basel, Switzerland):

    ______________________________________                                         LONZACURE ® M-DIPA                                                                         R.sub.1 = C.sub.3 H.sub.7 ; R.sub.2 = C.sub.3 H.sub.7 ;                        R.sub.3 = H                                                    LONZACURE ® M-DMA:                                                                         R.sub.1 = CH.sub.3 ; R.sub.2 = CH.sub.3 ; R.sub.3 = H          LONZACURE ® M-MEA:                                                                         R.sub.1 = CH.sub.3 ; R.sub.2 = C.sub.2 H.sub.5 ; R.sub.3                       = H                                                            LONZACURE ® M-DEA:                                                                         R.sub.1 = C.sub.2 H.sub.5 ; R.sub.2 = C.sub.2 H.sub.5 ;                        R.sub.3 = H                                                    LONZACURE ® M-MIPA:                                                                        R.sub.1 = CH.sub.3 ; R.sub.2 = C.sub.3 H.sub.7 ; R.sub.3                       = H                                                            LONZACURE ® M-CDEA:                                                                        R.sub.1 = C.sub.2 H.sub.5 ; R.sub.2 = C.sub.2 H.sub.5 ;                        R.sub.3 = Cl                                                   ______________________________________                                    

wherein R₁, R₂ and R₃ refer to the above chemical formula. The chemical names of these materials are as follows: M-DIPA is 4,4'-methylene-bis(2,6-diisopropylaniline), M-DMA is 4,4'-methylene-bis(2,6-dimethylaniline), M-MEA is 4,4'-methylene-bis(2-ethyl-6-methylaniline), M-DEA is 4,4'-methylene-bis(2,6-diethylaniline), M-MIPA is 4,4'-methylene-bis(2-isopropyl-6-methylaniline), and M-CDEA is 4,4'-methylene-bis(2,6-diethyl-3-chloroaniline). Lonzacure® M-CDEA is available in the United States from Air Products and Chemicals, Inc. (Allentown, Pa.). Particularly preferred second diamine curing agents are M-DIPA (methyl diisopropyl aniline) and M-DEA (methyl diethyl aniline).

Another diamine that may be used as a second diamine curing agent is trimethylene glycol di-para aminobenzoate, which is sold by Air Products and Chemicals, Inc. under the trade name Polacure 740M. It has the following formula: ##STR4##

The second diamine curing agent is preferably added to the first curing agent in an amount of from, for example, 2 to 80 percent, based on equivalents, with a preferred range being 2 to 60 percent. A more preferred amount of the second diamine curing agent is 10 to 50 percent by equivalents. The first diamine curing agent is present in an amount of, for example, 20 to 98 percent by equivalents, preferably 40 to 98 percent, and more preferably 50 to 90 percent by equivalents.

A preferred diamine curing agent system is a combination of DETDA and either M-DIPA or M-DEA. Preferably, DETDA comprises 70 to 100 weight percent, more preferably 80 to 90 weight percent, and most preferably about 85 percent by weight of the total weight of the diamine curing agent system. The M-DEA or M-DIPA, with M-DEA being most preferred, is preferably present in an amount of 5 to 30 percent, more preferably 10 to 20 percent, and most preferably 15 percent by weight of the total weight of the diamine curing agents.

Aliphatic Diisocyanates

The aliphatic diisocyanates have the basic formula O═C═N-A-N═C═O, wherein A is a straight, branched and/or cyclic aliphatic group having, for example, 6 to 13 carbon atoms. The aliphatic diisocyanates are preferably saturated diisocyanates.

A preferred aliphatic diisocyanate for use in the process of the present invention is 4,4'-dicyclohexylmethane diisocyanate. Three isomers of 4,4'-dicyclohexylmethane diisocyanate are shown below: ##STR5##

An example of such a diisocyanate is Desmodur W, a commercially available product of the Bayer Corporation. Desmodur W contains 20 percent of the trans, trans isomer of 4,4'-dicyclohexyl-methane diisocyanate, with the remaining 80 percent comprising the cis, trans and cis, cis isomers of 4,4'-dicyclohexyl-methane diisocyanate. XP-7041E, also available from the Bayer Corporation, contains 50 percent of the trans, trans isomer of 4,4'-dicyclohexylmethane diisocyanate, with the remaining 50 percent comprising the cis, trans and cis, cis isomers of 4,4'-dicyclohexyl-methane diisocyanate. Increasing the trans, trans isomer content from 20 to 50 percent improves the thermal properties and chemical resistance of the system with some degree of improvement in physical properties. Increasing the trans, trans isomer content to above 80 percent further improves the thermal stability and chemical resistance of the system with excellent physical properties and processing parameters.

Additional aliphatic diisocyanates that may be used include the following: First, 3-isocyanato-methyl-3,5,5-trimethylcyclohexyl isocyanate, which is available from Huls and has the following structural formula: ##STR6## Second, tetramethylxylene diisocyanate (either meta or para), which is available from Cytex and has the following structural formula: ##STR7##

Hydroxy-Containing Intermediates

The hydroxy-containing intermediates which can be used in the process of the invention are preferably polyester glycols and polyether glycols having a weight average molecular weight of, for example, about 500 to about 3000.

Polyester glycols that are useful in the present invention preferably have a weight average molecular weight of, for example, about 1250 to about 2000 and include polycaprolactones and polyesters based on esterification of aliphatic dicarboxylic acids of 2 to 12 carbon atoms, such as adipic, succinic, and sebacic acids, in the presence of aliphatic glycols having preferably 2 to 12 carbon atoms, such as ethylene glycol, propylene glycol, diethylene glycol, 1,4-butanediol, neopentyl glycol, 1,6-hexanediol, 1,10-decanediol, and 1,12-dodecanediol.

Suitable polycaprolactones may preferably be prepared by the addition reaction of E-caprolactone in the presence of aliphatic glycols having preferably 2 to 12 carbon atoms such as ethylene glycol, propylene glycol, diethylene glycol, 1,4-butanediol, neopentyl glycol, 1,6-hexanediol, 1,10-decanediol, and 1,12-dodecanediol. The resulting polycaprolactone has the following formula: ##STR8## where R=(CH₂)₂₋₁₂ and n is selected such that the average molecular weight of the prepolymer is within the preferred range of about 500 to 3,000, with an exemplary average molecular weight being about 1,900.

Polyesters of dicarboxylic acids and glycols can be prepared by esterification or transesterification procedures that are well known in the art.

Polyether glycols that are useful in the present invention preferably have a weight average molecular weight of, for example, about 1000 to about 3000 and include poly-1,2-propylene ether glycol, poly-1,3-propylene ether glycol, and polytetramethylene ether glycol (PTMEG). These polyether glycols may be prepared by condensing epoxides or other cyclic ethers according to procedures that are well known in the art.

Preferred hydroxy-containing intermediates for use in the process of the invention are polycaprolactones, especially the polycaprolactones prepared by the addition reaction of E-caprolactone in the presence of neopentyl glycol, 1,4-butanediol, 1,6-hexanediol, 1,10-decanediol, or 1,12-dodecanediol. The most preferred polycaprolactones are neopentyl glycol-initiated polycaprolactones.

Reaction Process

In the preferred method, the aliphatic diisocyanate is first mixed with at least one hydroxy-containing intermediate in an equivalent ratio of, for example, about two NCO groups, to one OH group. The mixture is then heated, for example at a temperature of 82° C. to 127° C. (180° F. to 260° F.), more preferably 93° C. to 115° C. (200° F. to 240° F.), for about 10 to 60 minutes, more preferably 30 to 45 minutes to form a prepolymer. The prepolymer is then reacted with a diamine curing agent at a temperature of about 71° C. to 107° C. (160° F. to 225° F.) for about 4 to 20 hours to form the cured elastomer. The diamine curing agent is preferably added to the prepolymer in an equivalent ratio of, for example, 0.95-1.06 NH₂ groups to 1.0 NCO group, with the range of 0.98-1.0 NH₂ groups to 1.0 NCO group being most preferred.

Alternatively, the aliphatic diisocyanate may be reacted with 0.3 to 0.8 equivalents of the hydroxy-containing intermediate to form a prepolymer, and then the remaining 0.2 to 0.8 equivalents of the hydroxy-containing intermediate are added with the diamine curing agent to form the cured elastomer.

The cured elastomer is then granulated and/or pelletized prior to extrusion of the final product.

Antiblocking agents/extrusion processing aids, such as for example N,N'-ethylene bisstearamides (Acrawax C) or N,N'-dioleoylethylenediamine (Glycolube VL), both available from Lonza Specialty Chemicals, may optionally be added to improve processing characteristics and minimize or eliminate blocking of the extrusion. Levels ranging from, for example, 0.25% to 2.0% by weight may be added during the manufacture of the thermoplastic polyurethane. Testing has shown that excellent anti-blocking of the extrudate takes place with the addition of 0.5% to 1.0% by weight of Glycolube VL with no change in the physical properties of the system. The above anti-blocking agents Acrawax C or Glycolube VL are preferably used in conjunction with flux-calcined diatomaceous earth, available from the Celite Corporation. The diatomaceous earth may also be used alone as the antiblocking agent/extrusion processing aid. The diatomaceous earth may be added in amounts ranging from, for example, 2.0 to 4.0% by weight to give excellent results. These antiblocking agents/extrusion processing aids are added in the form of a concentrate to either the granulated elastomer or during pelletizing. While the addition of diatomaceous earth does improve the processability of the polyurethanes, it can cause the moisture levels in the polyurethanes to increase, which can lead to undesirable effects such as hydrolysis and swelling of the polymer.

The resulting extrudable urea-extended polyurethanes combine excellent thermal properties with excellent physical properties at an "A" durometer of approximately 80.

The polyurethanes of the present invention may be extruded using conventional extruding devices well known in the art and commercially available. The polyurethanes are preferably extruded at a temperature of, for example, from about 215° C. to about 310° C. (about 420° F. to about 590° F.), more preferably from about 235° C. to about 260° C. (about 455° F. to about 500° F.). Typical pressure conditions of extrusion through a melt flow indexer are, for example, a load of about 6 to about 20 kg (corresponding to about 2,475 to about 8,249 psi of pressures, more preferrably a load of about 8 to about 13 kg (corresponding to about 3,299 to about 5,362 psi of pressures. The polyurethanes may preferrably be extruded into, for example, inflatable tubular structures or bladders for air bags.

Following extrusion, the polyurethanes will set to full stabilization and maximum cure properties in approximately 3 to 21 days under ambient conditions. Preferably, post-extrusion curing is effected by subjecting the extruded products to an elevated temperature in order to accelerate the stabilizing and curing process. For example, the extruded products may be subjected to a temperature of about 70° C. to 165° C. (about 160° F. to 325° F.), more preferrably about 95° C. to 110° C. (about 200° F. to 230° F.), for a period of about 4 to 24 hours, more preferrably about 12 to 16 hours.

The process of the present invention is illustrated by the following examples.

EXAMPLE 1

A clean reactor equipped with heating, cooling, vacuum, dry N₂, and an agitator is charged with Desmodur W (4,4'-dicyclohexylmethane diisocyanate containing 20% of the trans, trans isomer). The agitator is turned on. The temperature of the Desmodur W is increased to 71° C.

A mixture of diethylene glycol-initiated polycaprolactones, Tone 0240 (equivalent weight 1,000) and Tone 0230 (equivalent weight 625) both available from Union Carbide, is prepared. A sufficient amount of the Tone 0230 is added to the Tone 0240 such that when melted and mixed at 80° C., an equivalent weight of about 950 is achieved.

The polycaprolactone mixture is then added to the Desmodur W in an equivalent ratio of two NCO groups to one OH group. Heat and vacuum are turned on. When the temperature reaches approximately 100° C., the heat is turned off, and the reaction is allowed to exotherm to 110° to 121° C. When the reaction is completed and the temperature decreases to approximately 77° C., the resulting prepolymer is discharged from the reactor and filtered through a 200 mesh filter into clean containers. The containers are then purged with dry N₂ and sealed.

The prepolymer is then reacted with Ethacure 100 as the diamine curing agent in an equivalent ratio of 0.99 NH₂ groups to 1.0 NCO groups. With the prepolymer at a temperature of approximately 71° C., the Ethacure 100 at room temperature is added, and the components are thoroughly mixed. The mixture is then evacuated at 250 to 1,000 millitorr until it is bubble-free or only a few bubbles are breaking on the surface. The evacuated mixture is then cast into molds and cured for 8 to 16 hours at 105° C. The cast sheets were then granulated and pelletized to form extrudable thermoplastic elastomer pellets.

It is believed that the resulting elastomer has the following idealized formula: ##STR9## This formula shows the polycaprolactone/Desmodur W prepolymer with one of its NCO groups reacted with the NH₂ group from the Ethacure 100 diamine curing agent.

Table 1 shows a comparison of the rheological properties of (1) Pellethane 2102-80A, an extrudable grade hydroxyl-extended caprolactone polyester urethane commercially available from Dow with (2) the urea-extended urethane polymer resulting from the process of the present invention.

                                      TABLE 1                                      __________________________________________________________________________                   Pellethane 2102-80A                                                                         Present Invention                                   __________________________________________________________________________     Melt Flow Rate (MFR) D1238                                                                   190° C./8.7 kg/5.0 g/10 min                                                          230° C./8.7 kg/5.38 g/10                     __________________________________________________________________________                                min                                            

As can be seen from Table 1, the rheological properties of the polymer resulting from the process of the present invention are superior to those of the prior art polyurethane composition.

EXAMPLE 2

The physical properties of a sample of the cast polymer sheet resulting from Example 1 are determined and are set forth in Table 2. The cast sheet is approximately 70-75 mils thick.

The urethane polymer pellets resulting from Example 1 are melted and extruded to form inflatable tubular structures (ITS) which are then post-cured after extrusion. Post-cure time/temperature profiles evaluated are 2 and 4 hours at 110° C., 1.5 hours at 132° C., and 1 and 2 hours at 150° C. The physical properties of the extruded samples are then determined. Post-cured samples give very similar results. Sample thickness of the extruded material ranges from 22 to 28 mils. The physical properties of a representative sample of the post-cured extruded polymer are set forth in Table 2, which shows a comparison of the physical properties of Pellethane 2102-80A with the physical properties of the cast and extruded samples resulting from the process of the present invention.

                                      TABLE 2                                      __________________________________________________________________________                          Pellethane                                                                           Invention                                                                           Invention                                      Property             2102-80A                                                                             Cast ITS-6                                                                          Extruded ITS-6                                 __________________________________________________________________________     Tensile strength, psi                                                                           D412                                                                               5,800 7,500                                                                               8,400                                          Elongation, pct  D412                                                                               500   600  600                                            Tensile modulus, 100% elongation, psi                                                           D412                                                                               800   587  528                                            Tensile modulus, 200% elongation, psi                                                           D412                                                                               --    853  752                                            Tensile modulus, 300% elongation, psi                                                           D412                                                                               1,800 1,333                                                                               1,334                                          Tear strength, Die C, pli                                                                       D624                                                                               600   490  430                                            Tear strength, trouser split, pli                                                               D1938                                                                              --    320  250                                            E1ongation Set, pct                                                                             D412                                                                               50    16   30                                             Durometer hardness, A scale                                                                     D2240                                                                              81    83   80                                             __________________________________________________________________________

In Table 2, psi represents pounds per square inch; and pli represents pounds per linear inch.

As can be seen from Table 2, the physical properties of the composition resulting from the process of the present invention are superior to those of the prior art polyurethane composition. In addition, while the Pellethane 2102-80A is formulated for extrusion only, the polyurethane resulting from the process of the present invention can be liquid-cast, injection-molded, transfer-molded, sprayed, and/or extruded without changing its chemistry or stoichiometry.

EXAMPLE 3

Additional samples of the urethane polymer are prepared by the process of the invention using additional E-caprolactone polyesters in order to evaluate the physical properties and processing parameters of the resulting polymers. The E-caprolactone polyesters are esterified using 1,6-hexanediol and neopentyl glycol as initiators. These E-caprolactone polyesters are available from Solvay Interox of the UK. The E-caprolactone polyesters that are used in this example are as follows: CAPA 162/034 and CAPA 306/001 are 1,6-hexanediol-initiated polycaprolactones; CAPA 216 and CAPA 225 are neopentyl glycol-initiated polycaprolactones.

In addition, the effect of increasing the trans, trans ratio of the diisocyanate on the properties of the cured elastomer is evaluated. The diisocyanate used for this evaluation is XP-7041E, which contains 50% of the trans, trans isomer of 4,4'-dicyclohexylmethane diisocyanate.

The same process as Example 1 is used to prepare the prepolymers, except that the XP-7041E is melted at 80° C. and thoroughly mixed prior to use. The respective E-caprolactone polyesters are melted at 80° C. and then blended to give an equivalent weight of 950 prior to reacting with the diisocyanate to form the prepolymer. The E-caprolactone polyesters are added to the diisocyanate (XP-7041E) in an equivalent ratio of two NCO groups to one OH group. While this process substantially duplicates the prepolymer preparation process in Example 1, it provides a better understanding of the effect on physical, thermal, and processing properties related to changing initiators in the esterification of E-caprolactone and increasing the trans, trans ratio of the diisocyanate.

The curing agents used in this example are diethylene toluenediamine (DETDA) (samples ITS-7 to ITS-10) and a 95:5 equivalent mixture of DETDA and M-DIPA (sample ITS-10G-1). The ratio of NH₂ groups to NCO groups is maintained at 1:1.

Samples are mixed, evacuated, cast, and cured as in Example 1. The physical properties of the resulting cured elastomer samples are then determined.

The results are set forth in Table 3.

                                      TABLE 3                                      __________________________________________________________________________                      ITS-7 ITS-8   ITS-9   ITS-10 ITS-10G-1                                         Tone 0240                                                                            CAPA 162/034                                                                           CAPA 162/034                                                                           CAPA 225                                                                              CAPA 225                                          Tone 0230                                                                            CAPA 306/001                                                                           CAPA 306/001                                                                           CAPA 216                                                                              CAPA 216                                          XP-7041E                                                                             Desmodur W                                                                             XP-7041 Desmodur W                                                                            Desmodur W                       Property         DETDA DETDA   DETDA   DETDA  DETDA/M-DIPA                     __________________________________________________________________________     Tensile strength, psi                                                                           7,354 8,523   8,803   7,622  7,702                            Elongation, pct  605   600     615     600    600                              Tensile modulus, 100% elongation, psi                                                           656   609     625     563    541                              Tensile modulus, 200% elongation, psi                                                           944   985     935     845    793                              Tensile modulus, 300% elongation, psi                                                           1,528 1,385   1,485   1,239  1,183                            Tear strength, Die C, pli                                                                       448   475     525     455    430                              Tear strength, trouser split, pli                                                               382   305     325     310    297                              Tensile set after break, %                                                                      19    16      18      10     12                               Durometer Hardness, A scale                                                                     85    83      84      81     81                               __________________________________________________________________________

The physical properties of the systems documented in Table 3 are excellent. The thermal resistance of the samples that are prepared using XP-7041E, which contains 50 percent of the trans, trans isomer, is superior to that of the samples prepared using Desmodur W, which contains only 20 percent of the trans, trans isomer of 4,4'-dicyclohexylmethane diisocyanate.

EXAMPLE 4

The thermal stability and blocking characteristics of the samples resulting from Examples 2 and 3 are determined by heat aging in a Blue M forced-air circulating oven for 410 hours at 110° C.

The blocking evaluation consists of placing samples of the cast or extruded bladder material into the oven both with and without weight being applied. The weight is placed across the center of the sample, and in the case of the extruded samples, parallel to extrusion. The force applied is approximately 2.0 psi. After 410 hours, all samples are removed from the oven, allowed to cool to room temperature, and the bladder material is evaluated for blocking. No blocking of any of the samples occurs during the 410 hour/110° C. thermal aging test.

Table 4 shows the physical properties of the heat-aged samples:

                                      TABLE 4                                      __________________________________________________________________________                 ITS-6                                                                               ITS-6                                                         Property    Cast Extruded                                                                             ITS-7                                                                               ITS-8                                                                               ITS-9                                                                               ITS-10                                   __________________________________________________________________________     Tensile strength, psi                                                                      7,800                                                                               8,320 8,120                                                                               8,383                                                                               7,845                                                                               7,771                                    Elongation, pct                                                                            550  550   500  500  500  500                                      Tensile modulus, 100%                                                                      628  528   706  657  684  629                                      elongation, psi                                                                Tensile modulus, 200%                                                                      889  800   1,059                                                                               1,015                                                                               1,043                                                                               971                                      elongation, psi                                                                Tensile modulus, 200%                                                                      1,556                                                                               1,440 1,765                                                                               1,612                                                                               1,635                                                                               1,571                                    elongation, psi                                                                Die C tear, pli                                                                            410  352   382  425  422  400                                      Trouser tear, pli                                                                          125  178   125  203  222  191                                      Tensile set, pct                                                                           13   28    13   13   13   9                                        Hardness, A scale                                                                          84   --    87   84   86   84                                       __________________________________________________________________________

As shown in Table 4, all of the samples that are evaluated show good retention of physical properties with no blocking of the cast or extruded bladder material after heat-aging at 110° C. for 410 hours.

EXAMPLE 5

Additional polyurethane samples are prepared according to the process of Example 1 using neopentyl glycol-initiated polycaprolactones (CAPA 216 and CAPA 225) as the hydroxy-containing intermediate and Desmodur W as the aliphatic diisocyanate.

The diamine curing agents used in this example are diethylene toluene diamine (DETDA) (sample 10G) and a 70:30 equivalent mixture of DETDA and M-DIPA (sample 10G-3). The diamine curing agent is added to the prepolymer in an equivalent ratio of 1.02 NH₂ groups to 1.0 NCO group or 1.06 NH₂ groups to 1.0 NCO group (see Table 5). The cured polymer is cast into a sheet 72 mils thick. The cast sheets are then post-cured for 16 hours at 105° C. followed by aging for 7 days at room temperature. One set of samples is then further exposed to thermal aging for 30 days at 105° C. Another set of samples is then further exposed to hydrolytic aging for 30 days in distilled water at 71° C. The physical properties of the cast sheets are set forth in Table 5.

                                      TABLE 5                                      __________________________________________________________________________                      ITS-10G        ITS-10G                                                         1.0 NCO/1.02 NH.sub.2                                                                         1.0 NCO/1.06 NH.sub.2                          PROPERTY         S    T    H    S    T    H                                    __________________________________________________________________________     Tensile Strength, psi                                                                           7,583                                                                               7,111                                                                               7,557                                                                               6,265                                                                               6,101                                                                               6,577                                Elongation, %    550  520  560  563  525  650                                  Tensile modulus, 100% elongation, psi                                                           634  679  634  586  684  588                                  Tensile modulus, 200% elongation, psi                                                           894  997  889  856  1,019                                                                               829                                  Tensile modulus, 300% elongation, psi                                                           1,453                                                                               1,648                                                                               1,389                                                                               1,257                                                                               1,580                                                                               1,221                                Trouser Tear, pli     202            286                                       Elongation Set, %                                                                               11   11   11   13   9    17                                   A Hardness       83   84   83   82   84   82                                   __________________________________________________________________________                      ITS-10G-3      ITS-10G-3                                                       1.0 NCO/1.02 NH.sub.2                                                                         1.0 NCO/1.06 NH.sub.2                          PROPERTY         S    T    H    S    T    H                                    __________________________________________________________________________     Tensile Strength, psi                                                                           6,523                                                                               6,010                                                                               6,248                                                                               6,188                                                                               5,644                                                                               5,136                                Elongation, %    525  480  587  600  495  650                                  Tensile modulus, 100% elongation, psi                                                           573  638  515  562  648  504                                  Tensile modulus, 200% elongation, psi                                                           866  983  780  833  947  724                                  Tensile modulus, 300% elongation, psi                                                           1,368                                                                               1,606                                                                               1,208                                                                               1,235                                                                               1,566                                                                               1,048                                Trouser Tear, pli     214            236                                       Elongation Set, %                                                                               9    6    11   13   9    16                                   A Hardness       81   84   79   81   84   78                                   __________________________________________________________________________

In Table 5, "S" refers to the standard unaged samples; "T" refers to the thermal aged samples; and "H" refers to the hydrolytic aged samples.

EXAMPLE 6

A further polyurethane sample is prepared in the same manner as Example 5, except that the diamine curing agent used in this example is a 70:30 equivalent mixture of DETDA and M-DIPA, and the diamine curing agent is added to the prepolymer in an equivalent ratio of 0.98 NH₂ groups to 1.0 NCO group. Further, one sample is prepared without the addition of any antiblocking agents/extrusion processing aids, while to another sample 0.25 wt. % Acrawax C ("Wax") and 2.0 wt. % flux-calcined diatomaceous earth ("Floss") is added. The cast polyurethane sheet is extruded to form a sheet 21 to 25 mils thick. The post-cured extruded sheet is exposed to hydrolytic aging for 43 days in distilled water at 71° C. The physical properties of the hydrolytic-aged samples are set forth in Table 6.

                  TABLE 6                                                          ______________________________________                                                            ITS-10G-3  ITS-10G-3                                                           NO WAX     0.25% WAX                                        PROPERTY           NO FLOSS   2.0% FLOSS                                       ______________________________________                                         Tensile Strength, psi                                                                             6,373      6,385                                            Elongation, %      575        600                                              Tensile modulus, 100% elongation, psi                                                             531        548                                              Tensile modulus, 200% elongation, psi                                                             807        807                                              Tensile modulus, 300% elongation, psi                                                             1,289      1,290                                            Elongation Set, %  22         28                                               ______________________________________                                    

EXAMPLE 7

An additional polyurethane sample is prepared according to the process of Example 1, using polytetramethylene ether glycol (PTMEG) having a weight average molecular weight of 1000 as the hydroxy-containing intermediate. The PTMEG is added to the Desmodur W in an equivalent ratio of 1.45-1.65 NCO groups to 1.0 OH group. The prepolymer is reacted with a 70:30 equivalent mixture of DETDA and M-DIPA as the diamine curing agent, which is added to the prepolymer in an equivalent ratio of 0.98-1.0 NH₂ groups to 1.0 NCO groups. The cured polymer is cast into a sheet 72 mils thick. The resulting polyurethane has excellent extrusion parameters and a shore "A" hardness of 75. The physical properties of the cast sheet are set forth in Table 7.

                                      TABLE 7                                      __________________________________________________________________________                      71° C.                                                                              105° C.                                                     WATER IMERSION                                                                             THERMAL AGING                                                      (DAYS)      (DAYS)                                            PROPERTY   STANDARD                                                                             23  43  63  15   60                                           __________________________________________________________________________     Tensile, psi                                                                              5,136 5,463                                                                              5,273                                                                              5,602    4,512                                        Elongation, %                                                                             450   490 450 465      420                                          Tensile modulus, 100%                                                                     470   418 418 424      522                                          elongation, psi                                                                Tensile modulus, 200%                                                                     714   657 657 667      870                                          elongation, psi                                                                Tensile modulus, 300%                                                                     1,286 1,224                                                                              1,194                                                                              1,197    1,583                                        elongation, psi                                                                Elongation Set, %                                                                         3     5   0.8 3        5                                            Hardness, A Scale                                                                         76    75  74  76       76                                           __________________________________________________________________________

EXAMPLE 8

Example 7 is repeated using polytetramethylene ether glycol (PTMEG) having a weight average molecular weight of 2000 as the hydroxy-containing intermediate, which is reacted with Desmodur W in an equivalent ratio of 2.0 NCO groups to 1.0 OH group. The physical properties of a 72 mils thick cast sheet are set forth in Table 8.

                                      TABLE 8                                      __________________________________________________________________________                      71° C.                                                                              105° C.                                                     WATER IMERSION                                                                             THERMAL AGING                                                      (DAYS)      (DAYS)                                            PROPERTY   STANDARD                                                                             23  43  63  15  30  60                                        __________________________________________________________________________     Tensile, psi                                                                              5,099 5,275                                                                              4,538                                                                              5,294                                                                              5,020                                                                              4,386                                                                              3,716                                     Elongation, %                                                                             500   508 505 530 475 450 520                                       Tensile modulus, 100%                                                                     620   638 592 620 640 657 482                                       elongation, psi                                                                Tensile modulus, 200%                                                                     958   928 896 887 1,000                                                                              1,034                                                                              901                                       elongation, psi                                                                Tensile modulus, 300%                                                                     1,549 1,507                                                                              1,408                                                                              1,414                                                                              1,743                                                                              1,743                                                                              1,373                                     elongation, psi                                                                Elongation Set, %                                                                         13    13  9   14  6   14  22                                        Hardness, A Scale                                                                         85    85  82  83  84  86  83                                        __________________________________________________________________________

EXAMPLE 9

The ASTM D-1238 method for measuring the melt flow index is modified to reduce the dwell time. The following procedure is used to measure the melt flow index of the polyurethanes of the present invention. A temperature of 220° C. to 250° C. and a load of 7.0 kg to 12.5 kg is used depending on the composition of the polyurethane. A five gram sample of the polyurethane elastomer is charged to the melt flow indexer. A 30 second time frame is used to pack the pellets or granulated elastomer, after which time an additional dwell time of 150 seconds is used (for a total of 3 minutes) before applying the weight. The total five gram charge is extrudable for evaluation. Evaluation consists of appearance, diameter change from start to finish, time to extrude and strength by pulling on the extruded ribbon.

In general, evaluation in accordance with this method of samples prepared in accordance with the present invention has shown that the first portion of the extrusion is very strong, while the last portion is weak. However, after 24 hours there is a significant increase in the strength of the last portion, and after 7 to 14 days, all properties have fully recovered so that the strength of the extrusion is the same from front to end.

The foregoing disclosure of embodiments of the invention has been presented for the purposes of illustration and description. It is not intended to be exhaustive or to limit the invention to the precise form disclosed. Variations and modifications of the embodiments described herein will be obvious to one of ordinary skill in the art. The scope of the invention is to be defined only by the claims appended hereto. 

What is claimed is:
 1. An extrudable thermoplastic elastomeric urea-extended polyurethane comprising the reaction product of:(a) a polyurethane prepolymer comprising the reaction product of at least one aliphatic diisocyanate with at least one hydroxy-containing intermediate selected from the group consisting of polyester glycols, polyether glycols, and mixtures thereof, (b) at least one first diamine curing agent selected from the group consisting of 2,4-diamino-3,5-diethyl-toluene, 2,6-diamino-3,5-diethyl-toluene, and methylene dianiline, and (c) at least one second diamine curing agent selected from the group consisting of 4,4'-methylene-bis(2,6-diisopropylaniline), 4,4'-methylene-bis(2,6-dimethylaniline), 4,4'-methylene-bis(2-ethyl-6-methylaniline), 4,4'-methylene-bis(2,6-diethylaniline), 4,4'-methylene-bis(2-isopropyl-6-methylaniline), 4,4'-methylene-bis(2,6-diethyl-3-chloroaniline), and trimethylene glycol di-para aminobenzoate.
 2. The polyurethane according to claim 1, wherein the at least one first diamine curing agent comprises 20 to 98 percent by equivalents of a total amount of diamine curing agents, and the at least one second diamine curing agent comprises 2 to 80 percent by equivalents of the total amount of diamine curing agents.
 3. The polyurethane according to claim 1, wherein the at least one first diamine curing agent comprises 40 to 98 percent by equivalents of a total amount of diamine curing agents, and the at least one second diamine curing agent comprises 2 to 60 percent by equivalents of the total amount of diamine curing agents.
 4. The polyurethane according to claim 1, wherein the at least one aliphatic diisocyanate is selected from the group consisting of 4,4'-dicyclohexylmethane diisocyanate, 3-isocyanato-methyl-3,5,5-trimethylcyclohexyl isocyanate, and tetramethylxylene diisocyanate.
 5. The polyurethane according to claim 1, wherein the at least one aliphatic diisocyanate is 4,4'-dicyclohexylmethane diisocyanate.
 6. The polyurethane according to claim 5, wherein the 4,4'-dicyclohexylmethane diisocyanate contains at least 20 weight percent of a trans, trans isomer of 4,4'-dicyclohexylmethane diisocyanate.
 7. The polyurethane according to claim 5, wherein the 4,4'-dicyclohexylmethane diisocyanate contains at least 50 weight percent of the trans, trans isomer of 4,4'-dicyclohexylmethane diisocyanate.
 8. The polyurethane according to claim 5, wherein the 4,4'-dicyclohexylmethane diisocyanate contains at least 80 weight percent of the trans, trans isomer of 4,4'-dicyclohexylmethane diisocyanate.
 9. The polyurethane according to claim 1, wherein the at least one hydroxy-containing intermediate has a weight average molecular weight of about 500 to about
 3000. 10. The polyurethane according to claim 9, wherein the at least one hydroxy-containing intermediate is a polyester glycol comprising at least one polycaprolactone which has been prepared by the addition reaction of caprolactone in the presence of at least one aliphatic glycol having 2 to 12 carbon atoms.
 11. The polyurethane according to claim 10, wherein said at least one aliphatic glycol is selected from the group consisting of ethylene glycol, diethylene glycol, 1,4-butane diol, neopentyl glycol, 1,6-hexanediol, 1,10-decanediol, 1,12-dodecanediol, and mixtures thereof.
 12. The polyurethane according to claim 9, wherein the at least one hydroxy-containing intermediate is a polyester glycol comprising at least one polyester which has been prepared by condensing at least one aliphatic dicarboxylic acid having 2 to 12 carbon atoms in the presence of at least one aliphatic glycol having 2 to 12 carbon atoms.
 13. The polyurethane according to claim 12, wherein the at least one aliphatic dicarboxylic acid is selected from the group consisting of adipic acid, succinic acid, sebacic acid, and mixtures thereof.
 14. The polyurethane according to claim 12, wherein the at least one aliphatic glycol is selected from the group consisting of ethylene glycol, diethylene glycol, 1,4-butane diol, neopentyl glycol, 1,6-hexanediol, 1,10-decanediol, 1,12-dodecanediol, and mixtures thereof.
 15. The polyurethane according to claim 9, wherein the at least one hydroxy-containing intermediate is a polyether glycol comprising polytetramethylene ether glycol.
 16. The polyurethane according to claim 2, wherein the first diamine curing agent is selected from the group consisting of 2,4-diamino-3,5-diethyl-toluene, 2,6-diamino-3,5-diethyl-toluene, and mixtures thereof, and the second diamine curing agent is 4,4'-methylene-bis(2,6-diethylaniline).
 17. The polyurethane according to claim 1, wherein the extrudable thermoplastic urethane has a shore A hardness of about 80 and a melt flow index ranging from about 5 to 40 inches per minute when measured in accordance with ASTM D-1238, modified to reduce dwell time.
 18. A process for making an extrudable thermoplastic elastomeric urea-extended polyurethane comprising the steps of:(a) reacting at least one aliphatic diisocyanate with at least one hydroxy-containing intermediate selected from the group consisting of polyester glycols and polyether glycols, to form a prepolymer, and (b) reacting said prepolymer with at least one first diamine curing agent selected from the group consisting of 2,4-diamino-3,5-diethyl-toluene, 2,6-diamino-3,5-diethyl-toluene, and methylene dianiline, and with at least one second diamine curing agent selected from the group consisting of 4,4'-methylene-bis(2,6-diisopropylaniline), 4,4'-methylene-bis(2,6-dimethylaniline), 4,4'-methylene-bis(2-ethyl-6-methylaniline), 4,4'-methylene-bis(2,6-diethylaniline), 4,4'-methylene-bis(2-isopropyl-6-methylaniline), 4,4'-methylene-bis(2,6-diethyl-3-chloroaniline), and trimethylene glycol di-para aminobenzoate.
 19. The process according to claim 18, wherein the process is conducted in an environment containing no more than 0.03 weight percent of water based on the weight of total ingredients.
 20. The process according to claim 18, wherein the at least one aliphatic diisocyanate is mixed with the at least one hydroxy-containing intermediate in an equivalent ratio of two NCO groups to one OH group.
 21. The process according to claim 18, wherein the process further comprises pelletizing the polyurethane formed.
 22. The process according to claim 18, wherein the process further comprises extruding the polyurethane formed.
 23. A process for forming a product comprising(a) heating a thermoplastic elastomeric urea-extended polyurethane comprising the reaction product of at least one aliphatic diisocyanate, at least one hydroxy-containing intermediate selected from the group consisting of polyester glycols, polyether glycols, and mixtures thereof, and at least one diamine curing agent comprising at least one member selected from the group consisting of 2,4-diamino-3,5-diethyl-toluene, 2,6-diamino-3,5-diethyl-toluene, and methylene dianiline, and at least one member selected from the group consisting of 4,4'-methylene-bis(2,6-diisopropylaniline), 4,4'-methylene-bis(2,6-dimethylaniline), 4,4'-methylene-bis(2-ethyl-6-methylene), 4,4'-methylene-bis(2,6-diethylaniline), 4,4'-methylene-bis(2-isopropyl-6-methylaniline), 4,4'-methylene-bis(2,6-diethyl-3-chloroaniline), and trimethylene glycol di-para aminobenzoate, and (b) extruding the heated polyurethane to form an extruded product.
 24. The process according to claim 23, wherein the extruding is conducted at a temperature of about 215° C. to about 310° C.
 25. The process according to claim 23, wherein the extruding is conducted at a pressure of about 3299 to about 5362 psi.
 26. The process according to claim 23, wherein the process further comprises post curing the extruded product.
 27. An extruded polyurethane product formed by the process of claim
 23. 28. An extruded polyurethane product according to claim 27, wherein said product is an inflatable tubular structure. 